VELCRETE 003 ZSC
Technical Datasheet
SHARADAA VELCRETE 003 ZSC
PRODUCT DATA SHEET: SHARADAA VELCRETE 003 ZSC
Aggregate : High Purity Sintered Mullite/Silicon Carbide/Zircon
Bond : Ultra Fine (Abrasion, Alkali and Thermal Shock Resistance)
Type of Setting : Hydraulic
Water required for casting : 4.5 – 5%
Application Method : Vibrocasting
Form De-moulding Time : 8 hour
Packing : Dry powder will be packed in 25 kgs Poly-lined HDPE bags
Shelf Life : 9 months
| Property | Unit | Specification | Test Method (Part Reference) |
|---|---|---|---|
| Service Temperature | °C | 1600 (max) | BIS 10570 |
| Maximum Grain Size | mm | 10 (max) | BIS 10570 |
| Bulk Density Dried at 110°C/24 hrs | gm/cc | 2.55 (min) | BIS 10570 |
| Cold Crushing Strength Dried at 110°C/24 hrs | kg/cm² | 1000 (min) | BIS 10570 |
| Cold Crushing Strength Fired at 1100°C/3 hrs | kg/cm² | 1200 (min) | BIS 10570 |
| Cold Crushing Strength Fired at 1300°C/3 hrs | kg/cm² | 1200 (min) | BIS 10570 |
| Permanent Linear Change Fired at 1500°C/3 hrs | % | +0.5 | BIS 10570 |
| Abrasion Loss | cc | 3 (max) | ASTM C704 |
| Alkali Resistance | Scale (0-10) | 1 | ASTM C454 |
| Chemical Analysis | |||
| Al₂O₃ | % | 40 - 45 | BIS 12107 |
| SIC | % | 12 - 15 | XRF |
| ZrO2 | % | 3 - 5 | XRF |
| SiO2 | % | 30 - 35 | BIS 12107 |
| Fe₂O₃ | % | 0.8 | BIS 12107 |
NOTE:
- The properties shown are for vibratory cast material only unless specified otherwise
- Water requirement indicated are based on laboratory test conditions. Actual water requirement may vary subject to site conditions
- Types of Mixer Paddle type with 33 RPM