Nanobond 80 AL
Product Datasheet
NANOBOND 80 AL
Nanobond Castable for Aluminium Industry
PRODUCT DATA SHEET: NANOBOND 80 AL
| PROPERTIES | TYPICAL VALUES |
|---|---|
| Product Characteristics | |
| Type of Bond | Nano bond |
| Type of Setting | Hydraulic |
| Aggregate | Cal. Bauxite |
| Service Temp °C (Max) | 1300 |
| Maximum Grain Size (mm) | 10 |
| Chemical Properties | |
| Al2O3 (Min) | 80 |
| Fe203 (Max) | 1.8 |
| Physical Properties | |
| Bulk Density after drying at 110 °C/24 hrs (gm/cc) (Min) | 3.00 |
| Cold Crushing Strength (Kg/cm2) (Min) | |
| After drying at 110 °C / 24 hrs | 800 |
| After firing at 800 °C /3 hrs | 900 |
| After firing at 1200 °C /3 hrs | 1000 |
| Cold MOR (Kg/cm2) (Min) | |
| After drying at 110 °C /24 hrs | 160 |
| After firing at 1100 °C /3 hrs | 180 |
| After firing at 1500 °C /3 hrs | 200 |
| Thermal Properties | |
| Thermal Conductivity at 600°C hot face (Kcal/hr/m/°C ) (Max) | 1.8 |
| Reversible thermal Expansion at 1000°C (%) (Max) | 1.2 |
| Hot MOR at 1100°C (Kg/cm2) (Min) | 200 |
| Aluminium Resistance | Very Good |
| Apparent Porosity at 1200°C (%)(Max) | 14 |
| Permanent Linear Change at 1200°C(%)(Max) | +0.5 |
| Installation inputs | |
| Storage | Under Covered Shed |
| Shelf Life | 6 Months |
| Installation Method | Vibration |
| Water % | 4 - 5 |
| Setting Time | 6 Hrs |
| Machinery Required | Paddle Mixer |
| Material Required per M3 | 2800 Kg |
| Form demoulding time | 8 Hrs |
| Packaging | 25 Kg |
NOTE:
- Above are average typical test data subject to reasonable variations.
- Tested as per BIS 10570: 2009.