REFCAST LC 5010 TSR
Technical Datasheet
REFCAST LC 5010 TSR
Low Cement Castable for Cement Industry
PRODUCT DATA SHEET: SHARADAA REFCAST LC 5010 TSR
Aggregate : Corderite / Calcined Clay
Bond : Ultra Fine
Type of Setting : Hydraulic
Water required for casting : 7 – 8 %
Packing : Dry powder will be packed in 25 kgs Poly-lined HDPE bags
Shelf Life : 9 months
Application Method : Vibrocasting Form
De-moulding Time : 8 hour
| Properties | Unit | Specification | Test Method |
|---|---|---|---|
| Service Temperature | °C | 1300 (max) | BIS 10570 |
| Maximum Grain Size | mm | 6 (max) | BIS 10570 |
| Bulk Density dried at 110°C/24 hrs | gm/cc | 2.30 (min) | BIS 10570 |
| Cold Crushing Strength dried at 110°C/24 hrs | kg/cm2 | 550 (min) | BIS 10570 |
| Cold Crushing Strength Fired at 1100°C/3 hrs | kg/cm2 | 550 (min) | BIS 10570 |
| Modulus of Rupture Dried at 110°C/24 hrs | kg/cm2 | 100 (min) | BIS 10570 |
| Modulus of Rupture Fired at 1100°C/3 hrs | kg/cm2 | 100 (min) | BIS 10570 |
| Permanent Linear Change Fired at 1100°C/3 hrs | % | ± 0.3 | BIS 10570 |
| Chemical Analysis Al2O3 Fe2O3 Mgo | % | 45 (min) 2 (max) 3 (max) | BIS 12107 BIS 12107 BIS 12107 |
NOTE:
The properties shown are for vibratory cast material only unless specified otherwise
Water requirement indicated are based on laboratory test conditions. Actual water requirement may vary subject to site conditions
Types of Mixer Paddle type with 33 RPM